Ultralong Rutile TiO2 Nanowire Arrays for Highly Efficient Dye-Sensitized Solar Cells.

ACS applied materials & interfaces

PubMedID: 27097727

Li H, Yu Q, Huang Y, Yu C, Li RZ, Wang J, Guo F, Zhang Y, Zhang X, Wang P, Zhao L. Ultralong Rutile TiO2 Nanowire Arrays for Highly Efficient Dye-Sensitized Solar Cells. ACS Appl Mater Interfaces. 2016;.
Vertically aligned rutile TiO2 nanowire arrays (NWAs) with lengths of ~44 ┬Ám have been successfully synthesized on transparent, conductive fluorine-doped tin oxide (FTO) glass by a facile one-step solvothermal method. The length and wire-to-wire distance of NWAs can be controlled by adjusting the ethanol content in the reaction solution. By employing optimized rutile TiO2 NWAs for dye-sensitized solar cells (DSCs), a remarkable power conversion efficiency (PCE) of 8. 9% is achieved. Moreover, in combination with a light-scattering layer, the performance of a rutile TiO2 NWAs based DSC can be further enhanced, reaching an impressive PCE of 9. 6%, which is the highest efficiency for rutile TiO2 NWA based DSCs so far.